Votre recherche
Résultats 7 ressources
-
The production of natural gas hydrates will change the cementation strength, porosity, and effective stress in the stratum, which may lead to engineering and geological disasters. Sand production is a phenomenon where sand particles are carried out of the reservoir along with fluids during gas extraction, posing challenges to safe and sustainable production. This study explored the mechanism of fine particle migration in multiphase flow by a microscopic visualization test device. The device can inject a gas–liquid–solid phase at the same time and allow real-time observation. Experimental tests on fine particle migration of single- and two-phase fluid flow were carried out considering different conditions, i.e., fine particle concentration, fine particle size, fluid flow rate, and gas–liquid ratio. The results show that in single-phase fluid flow, the original gas will gradually dissolve in the liquid phase, and finally stay in the test device as bubbles, which can change the pore structures, resulting in the accumulation of fine particles at the gas–liquid interface. In two-phase fluid flow with mixed gas–water fluids, there are two flow modes of gas–liquid flow: mixed flow and separated flow. The interfacial tension at the gas–liquid interface can effectively migrate fine particles when the gas–liquid flows alternately and the sand production rate further increases as the gas–liquid ratio increases. In addition, changes in the concentration of fine particles, particle size, fluid flow rate, and the gas–liquid ratio will affect the migration of fine particles, leading to differences in the final sand production.
-
The deterioration of anhydrite rock exposed to a freeze–thaw environment is a complex process. Therefore, this paper systematically investigated the physical and mechanical evolutions of freeze–thawed anhydrite rock through a series of multi-scale laboratory tests. Meanwhile, the correlation between pore structure and macroscopic mechanical parameters was discussed, and the deterioration mechanisms of anhydrite rock under freeze–thaw cycles were revealed. The results show that with the increase in freeze–thaw processes, the mechanical strength, elastic modulus, cohesion, proportions of micropores (r ≤ 0.1 μm), and PT-Ipore throat (0–0.1 μm) decrease exponentially. In comparison, the mass variation, proportions of mesopores (0.1 μm < r < 1 μm), macropores (r ≥ 1 μm), and PT-II pore throat (0.1–4 μm) increase exponentially. After 120 cycles, the mean porosity increases by 66.27%, and there is a significant honeycomb and pitted surface phenomenon. Meanwhile, as the freeze–thaw cycles increase, the frost resistance coefficient decreases, while the damage variable increases. The correlation analysis between pore structure and macroscopic mechanical parameters shows that macropores play the most significant role in the mechanical characteristic deterioration of freeze–thawed anhydrite rock. Finally, it is revealed that the water–rock expansion and water dissolution effects play a crucial role in the multi-scale damage of anhydrite rock under the freeze–thaw environment.
-
Abstract Interdisciplinary research is considered a source of innovativeness and creativity, serving as a key mechanism for creating recombination necessary for the evolution of science systems. The aim of this study is to quantitatively establish the connection between interdisciplinary research and the research fronts that have recently emerged in civil engineering. The degree of interdisciplinarity of the research fronts was measured by developing metrics from bibliographic analyses. As indicated by the consistent increase in the metrics of interdisciplinarity over time, research fronts tend to emerge in studies with increasing diversity in the disciplines involved. The active disciplines involved in the fronts vary over time. The most active disciplines are no longer fundamental but those associated with energy, environment, and sustainable development, focusing on solutions to climate change and integrating intelligence technologies.
-
To study the mechanical and cracking modes of anhydrite rock under the freeze–thaw weathering process, the physico-mechanical characteristics and morphology evolutions of anhydrite samples were determined by a series of laboratory tests. Then, a numerical simulation model was established through the PFC2D program, and the types and number of cracks during the uniaxial compression conditions were analyzed. Finally, the distribution of maximum principal stress and shear stress was revealed. The results indicate that as the number of freeze–thaw cycles increases, there is a growth in the mass loss rate and macroscopic damage variables while the uniaxial compression strength and elastic modulus decrease exponentially. Under uniaxial compression stress, the proportion of tensile cracks in the anhydrite model is the highest, followed by tensile shear cracks and compressive shear cracks. As the number of freeze–thaw cycles increases, the proportion of tensile cracks increases exponentially, while the proportion of tensile shear cracks and compressive shear cracks decreases exponentially. Furtherly, it is found that the maximum principal stress and maximum shear stress extreme values decrease exponentially with the increase of freeze–thaw cycles. For example, after 120 cycles, the maximum shear stress at the peak stress point decreased by 47.3%. The research results will promote the comprehension of anhydrite rock geotechnical engineering disaster mechanisms in cold regions.